Microstructure analysis and low temperature degradation resistance of doped 3Y-TZP ceramics for hip implant application

Dinesh Ragurajan, Mohsen Golieskardi, Meenaloshini Satgunam, Angela Min Hwei Ng

Research output: Chapter in Book/Report/Conference proceedingConference contribution

Abstract

The effect of manganese oxide (MnO2) and aluminum oxide (Al2O3) addition of up to 1 wt% in yttria-stabilized tetragonal zirconia polycrystals (Y-TZP), sintered in air at 1450°C, was examined. The low temperature degradation resistance was observed by immersing the sample in Ringer solution at 37°C over a period of 8 weeks, whereby the weight loss and the SEM image of sample was analyzed to generate the degradation pattern of the sample. Additions of 0.6wt% Al2O3/ 0.4wt% MnO2 were found to be beneficial in retarding the ageing of the ceramics sample. Therefore the sample was deemed beneficial in the use of orthopedic applications.

Original languageEnglish
Title of host publicationMaterials and Technologies in Engineering Activity
EditorsPuneet Tandon, Poi Sim Khiew, Guojian Chen, Haider F. Abdul Amir
PublisherTrans Tech Publications Ltd
Pages42-47
Number of pages6
ISBN (Print)9783038357315
DOIs
Publication statusPublished - 01 Jan 2016
EventInternational Conference on Design, Materials and Manufacturing, ICDMM 2016 - Kuala Lumpur, Malaysia
Duration: 25 Mar 201627 Mar 2016

Publication series

NameKey Engineering Materials
Volume706
ISSN (Print)1013-9826

Other

OtherInternational Conference on Design, Materials and Manufacturing, ICDMM 2016
CountryMalaysia
CityKuala Lumpur
Period25/03/1627/03/16

Fingerprint

Degradation
Microstructure
Manganese oxide
Aluminum Oxide
Yttria stabilized zirconia
Polycrystals
Orthopedics
Aging of materials
Aluminum
Temperature
Scanning electron microscopy
Oxides
Air
Ringer's solution
manganese oxide
yttria stabilized tetragonal zirconia

All Science Journal Classification (ASJC) codes

  • Materials Science(all)
  • Mechanics of Materials
  • Mechanical Engineering

Cite this

Ragurajan, D., Golieskardi, M., Satgunam, M., & Ng, A. M. H. (2016). Microstructure analysis and low temperature degradation resistance of doped 3Y-TZP ceramics for hip implant application. In P. Tandon, P. S. Khiew, G. Chen, & H. F. A. Amir (Eds.), Materials and Technologies in Engineering Activity (pp. 42-47). (Key Engineering Materials; Vol. 706). Trans Tech Publications Ltd. https://doi.org/10.4028/www.scientific.net/KEM.706.42
Ragurajan, Dinesh ; Golieskardi, Mohsen ; Satgunam, Meenaloshini ; Ng, Angela Min Hwei. / Microstructure analysis and low temperature degradation resistance of doped 3Y-TZP ceramics for hip implant application. Materials and Technologies in Engineering Activity. editor / Puneet Tandon ; Poi Sim Khiew ; Guojian Chen ; Haider F. Abdul Amir. Trans Tech Publications Ltd, 2016. pp. 42-47 (Key Engineering Materials).
@inproceedings{4ed74e8ecc3147ea9e5de426bf947061,
title = "Microstructure analysis and low temperature degradation resistance of doped 3Y-TZP ceramics for hip implant application",
abstract = "The effect of manganese oxide (MnO2) and aluminum oxide (Al2O3) addition of up to 1 wt{\%} in yttria-stabilized tetragonal zirconia polycrystals (Y-TZP), sintered in air at 1450°C, was examined. The low temperature degradation resistance was observed by immersing the sample in Ringer solution at 37°C over a period of 8 weeks, whereby the weight loss and the SEM image of sample was analyzed to generate the degradation pattern of the sample. Additions of 0.6wt{\%} Al2O3/ 0.4wt{\%} MnO2 were found to be beneficial in retarding the ageing of the ceramics sample. Therefore the sample was deemed beneficial in the use of orthopedic applications.",
author = "Dinesh Ragurajan and Mohsen Golieskardi and Meenaloshini Satgunam and Ng, {Angela Min Hwei}",
year = "2016",
month = "1",
day = "1",
doi = "10.4028/www.scientific.net/KEM.706.42",
language = "English",
isbn = "9783038357315",
series = "Key Engineering Materials",
publisher = "Trans Tech Publications Ltd",
pages = "42--47",
editor = "Puneet Tandon and Khiew, {Poi Sim} and Guojian Chen and Amir, {Haider F. Abdul}",
booktitle = "Materials and Technologies in Engineering Activity",

}

Ragurajan, D, Golieskardi, M, Satgunam, M & Ng, AMH 2016, Microstructure analysis and low temperature degradation resistance of doped 3Y-TZP ceramics for hip implant application. in P Tandon, PS Khiew, G Chen & HFA Amir (eds), Materials and Technologies in Engineering Activity. Key Engineering Materials, vol. 706, Trans Tech Publications Ltd, pp. 42-47, International Conference on Design, Materials and Manufacturing, ICDMM 2016, Kuala Lumpur, Malaysia, 25/03/16. https://doi.org/10.4028/www.scientific.net/KEM.706.42

Microstructure analysis and low temperature degradation resistance of doped 3Y-TZP ceramics for hip implant application. / Ragurajan, Dinesh; Golieskardi, Mohsen; Satgunam, Meenaloshini; Ng, Angela Min Hwei.

Materials and Technologies in Engineering Activity. ed. / Puneet Tandon; Poi Sim Khiew; Guojian Chen; Haider F. Abdul Amir. Trans Tech Publications Ltd, 2016. p. 42-47 (Key Engineering Materials; Vol. 706).

Research output: Chapter in Book/Report/Conference proceedingConference contribution

TY - GEN

T1 - Microstructure analysis and low temperature degradation resistance of doped 3Y-TZP ceramics for hip implant application

AU - Ragurajan, Dinesh

AU - Golieskardi, Mohsen

AU - Satgunam, Meenaloshini

AU - Ng, Angela Min Hwei

PY - 2016/1/1

Y1 - 2016/1/1

N2 - The effect of manganese oxide (MnO2) and aluminum oxide (Al2O3) addition of up to 1 wt% in yttria-stabilized tetragonal zirconia polycrystals (Y-TZP), sintered in air at 1450°C, was examined. The low temperature degradation resistance was observed by immersing the sample in Ringer solution at 37°C over a period of 8 weeks, whereby the weight loss and the SEM image of sample was analyzed to generate the degradation pattern of the sample. Additions of 0.6wt% Al2O3/ 0.4wt% MnO2 were found to be beneficial in retarding the ageing of the ceramics sample. Therefore the sample was deemed beneficial in the use of orthopedic applications.

AB - The effect of manganese oxide (MnO2) and aluminum oxide (Al2O3) addition of up to 1 wt% in yttria-stabilized tetragonal zirconia polycrystals (Y-TZP), sintered in air at 1450°C, was examined. The low temperature degradation resistance was observed by immersing the sample in Ringer solution at 37°C over a period of 8 weeks, whereby the weight loss and the SEM image of sample was analyzed to generate the degradation pattern of the sample. Additions of 0.6wt% Al2O3/ 0.4wt% MnO2 were found to be beneficial in retarding the ageing of the ceramics sample. Therefore the sample was deemed beneficial in the use of orthopedic applications.

UR - http://www.scopus.com/inward/record.url?scp=84984633338&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=84984633338&partnerID=8YFLogxK

U2 - 10.4028/www.scientific.net/KEM.706.42

DO - 10.4028/www.scientific.net/KEM.706.42

M3 - Conference contribution

SN - 9783038357315

T3 - Key Engineering Materials

SP - 42

EP - 47

BT - Materials and Technologies in Engineering Activity

A2 - Tandon, Puneet

A2 - Khiew, Poi Sim

A2 - Chen, Guojian

A2 - Amir, Haider F. Abdul

PB - Trans Tech Publications Ltd

ER -

Ragurajan D, Golieskardi M, Satgunam M, Ng AMH. Microstructure analysis and low temperature degradation resistance of doped 3Y-TZP ceramics for hip implant application. In Tandon P, Khiew PS, Chen G, Amir HFA, editors, Materials and Technologies in Engineering Activity. Trans Tech Publications Ltd. 2016. p. 42-47. (Key Engineering Materials). https://doi.org/10.4028/www.scientific.net/KEM.706.42